A 556 / A 556m Grade A2 Seamless Boiler Tubes Carbon Steel

precision seamless boiler tubes

a 556 seamless boiler tubes

precision carbon steel boiler tubes

Place of Origin:

China

Brand Name:

Torich

Certification:

ISO9001

Request A Quote

Product Details

Application:

Boiler

Grade:

A2, B2, C2

Supply Ability:

60000 Ton Per Year

Standard:

ASTM A556

Highlight:

precision seamless boiler tubes

a 556 seamless boiler tubes

precision carbon steel boiler tubes

Payment & Shipping Terms

Minimum Order Quantity

2Ton

Price

USD2000-3000

Packaging Details

PACKING WOODEN CASE

Delivery Time

30-45

Payment Terms

L/C,D/A,D/P,T/T

Supply Ability

50000Ton per years

A500 Carbon Steel Square Tube High Strength Carbon Steel Structural Tubing For Building Structure

Get Best Price

video

AISI 4140 Seamless Tubing Medium Carbon Alloy Steel Seamless Pipe For Mechanical

Get Best Price

video

TP409 Ferritic Stainless Steel Seamless Tube For General Service

Get Best Price

video

ASME SA179 Seamless Carbon Steel Tubing Cold-Drawn Low-Carbon Steel Tube For Heat-Exchanger

Get Best Price

86-574-88086983

Contact Now

Product Description

A 556/A 556M Grade A2 Seamless Carbon Steel Boiler Tubes for Boiler Pipe

1.Standard Scope

1.1 This specifification2 covers minimum-wall-thickness,seamless cold-drawn carbon steel tubes

including bending into the form of U-tubes, if specifified,for use in tubular feedwater heaters.

1.2 The tubing sizes covered shall be 5 ⁄8 to 11 ⁄4-in. [15.9 to 31.8-mm] outside diameter, inclusive,

with minimum wall thicknesses equal to or greater than 0.045 in. [1.1 mm].

1.3 Optional supplementary requirements are provided, and when desired,shall be stated in the order.

2.Manufacture

(1)Manufactur-------Tubes shall be made by the seamless process and shall be cold drawn.

(2 )Heat Treatment:

2.2.1 Cold-drawn tubes shall be heat treated after the fifinal cold-draw pass at a temperature

of 1200°F[640°C] or higher to ensure ductility satisfactory for rolling into tube sheets and tomeet

mechanical properties as specifified.

2.2.2 If stress-relief anneal of the U-bends is specifified, the anneal shall consist of heating the bent

portion within a range of 1100 to 1200°F [585 to 640°C].

3.Chemical Requirement :

Element	Composition ,%
Element	Grade A2	Grade B2	Grade C2
Carbon, max	0.18	0.27	0.30
Manganese	0.27-0.63	0.29-0.93	0.29-1.06
Phosphorus, max	0.035	0.035	0.035
Sulfur, max	0.035	0.035	0.035
Silicon , min	...	0.10	0.10

4.Tensile Requirements:

	Grade A2	Grade B2	Grade C2
Tensile strength,min,ksi(Mpa)	47(320)	60(410)	70(480)
Yield Strength,min,ksi(Mpa)	26(180)	37(260)	40(280)
Elongation in 2 in or 50min, min,%(longitudinal)	35	30	30