High Strength Alloy Steel Seamless Tube / Pipe Hastelloy C For Petrochemical

Basic Information
Place of Origin: China
Brand Name: Torich
Certification: CE PED
Model Number: Hastelloy C
Minimum Order Quantity: 1000kg
Price: negotiable
Packaging Details: In bundles in wooden box
Delivery Time: 6-8 weeks
Payment Terms: L/C, T/T
Supply Ability: 200 tons per year
Detail Information
Material: Hastelloy C Similar Grade: UNS N10276 / W.Nr.2.4819 ...
Standard: ASTM B462,STM B564, ASTM B575... Melting Temperature Range: 1325 ~ 1370 ℃
Application: Chemical Industry And High-temperature Environments
High Light:

alloy steel tube

,

alloy steel seamless tube


Product Description

Alloy Steel Pipe Hastelloy C nickel-chromium-molybdenum alloy Welded steel pipe

 

Hastelloy C  is a nickel-chromium-molybdenum alloy containing tungsten content of silicon, carbon is very low.

 

Standard of Hastelloy C : ASTM B462,STM B564, ASTM B575 and so on

Hastelloy C is characterized by:

● In the oxidation and reduction status, for most corrosive medium has excellent corrosion resistance.
● excellent resistance to pitting, crevice corrosion and stress corrosion cracking.

 

Application areas:

In the chemical and petrochemical fields.

It has been widely used for applications such as contact elements and catalytic systems in chloride-containing organic compounds. Such materials are particularly suitable for use in high temperature, mixed with impurities of inorganic and organic acids (such as formic acid and acetic acid), corrosive seawater environment.

Other application areas:
● pulp and paper industry, such as digestion and bleach containers
● FGD scrubber system, reheater, moisture and other fans
● equipment and components in sour gas environment jobs
● acetic acid and acidic products reactor
● sulfuric acid condenser
● methylene diphenyl isocyanate (MDI)
● impure phosphoric acid production and processing

 

Hastelloy C  grades and standards:

Grades and Standards Material Grade specifications
chemical composition Pipe Sheet Bar Strip Wire Forging
Seamless Welded pipe
France
AFNOR
NC17D                
Germany
DIN
VdTÜV
W.Nr.2.4819
NiMo16Cr15W
17744
424
17751   17750
424
17752
424
17750 424  
United Kingdom
BS EN
                 
United States
ASTM
AME
UNS N10276   B622
SB622
B619/626
SB619/626
B575
SB575
B574
SB574
B575
SB575
  B366
SB366
ISO NiMo16Cr15Fe6W4                

 

Hastelloy C chemical composition:

Ni Cr Fe C Mn Si Mo W Co V P S
Margin 15.0-16.5 4-7 ≤0.01 ≤1 ≤0.08 15-17 3-4.5 ≤2.5 0.1-0.3 ≤0.015 ≤0.01


Hastelloy C Physical properties:

Density: ρ = 8.9g / cm3

melting temperature range: 1325 ~ 1370 ℃

 

The corrosion resistance of Hastelloy C:

Higher molybdenum and chromium content make Hastelloy C alloy can resist various aggressive chemical media, including reducing media, such as phosphoric acid, hydrochloric acid, sulfuric acid, chlorine, chlorine-containing organic or inorganic media. Due to the high nickel content, Hastelloy C can effectively resist chlorine caused due to stress corrosion cracking, and even hot chloride solution.

Time - Temperature - sensitized curve (0.008% carbon content, with reference to ASTM G28 Method A)

1

 

Hastelloy C Application:

Hastelloy C has been widely used in most of the chemical industry and high-temperature environments.

Typical fields of application:

● flue gas desulfurization system

● pickling and acid regeneration plant

● production of acetic acid and agrochemicals

● production of titanium dioxide (chloride method)

● electrolytic plating

 

 

Hastelloy C processing and heat treatment:

1.Hastelloy C alloy by traditional production process manufacturing and processing.
2. Before the heat treatment and heat treatment process should always be kept clean and pollution-free workpieces.
3. It should fully take into account the sensitivity of sensitized when the alloy rapid cooling at 1000 ℃ ~ 600 ℃ between.
4. In the heat treatment process can not contact with sulfur, phosphorus, lead and other low melting point metal, otherwise it will impair the performance of the alloy, such as marking paint should pay attention to clear, the temperature indicating paint, crayons, oil, fuel and other contaminants.
5. The fuel sulfur content as low as possible, the sulfur content of natural gas should be less than 0.1%, heavy oil should be less than 0.5% sulfur content. ʱ??
6. furnace gas furnace with a neutral to slightly oxidizing appropriate, should avoid furnace gas fluctuates between oxidation and reduction, heated by the flame is not burning directly to the workpiece.

 

Hastelloy C Heating:

Before the heat treatment and heat treatment process should always be kept clean and pollution-free workpieces.

During the heat treatment can not touch the sulfur, phosphorus, lead and other low melting point metal, otherwise Nicrofer 6616 hMo alloy becomes brittle, should pay attention to remove paint, such as tags, temperature indicating paint, crayons, oil, fuel and other contaminants. Fuel sulfur content as low as possible, the sulfur content of natural gas should be less than 0.1%, heavy oil should be less than 0.5% sulfur content. Electric heating is a better choice, because precise temperature furnace, furnace gas and clean. If the gas furnace gas furnace clean enough, you can choose from.

Furnace gas furnace with a neutral to slightly reducing appropriate, should avoid furnace gas fluctuates between oxidation and reduction, heated by the flame is not burning directly to the workpiece.

 

Heat treatment:

1.Hastelloy C thermal processing temperature range of 1200 ℃ ~ 950 ℃, cooling method for cooling or rapid air cooling.
2. To ensure the best corrosion resistance, thermal processing should be carried out after the heat treatment, the workpiece should be directly added to the warmed heat treatment furnaces. ʱ??

 

cold machelloning:

Work hardening rate 1.Hastelloy C is greater than the austenitic stainless steel, so the need for processing equipment selection. Workpiece should state solution heat treatment, and there should be an intermediate annealing during cold. ʱ??

2. If the cold rolling is greater than 15%, you need a secondary solution treatment of the workpiece.

 

Hastelloy C Heat Treatment:

1.Hastelloy C solution treatment temperature range 1100 ℃ ~ 1160 ℃.
2. The cooling method is water quenching, the material thickness of less than 1.5mm can also be used to quickly cooled. The use of air-cooled, it should be within 2 minutes of cooling from 1000 ℃ to 600 ℃.
3. During the heat treatment, the workpiece must be kept clean.

 

Hastelloy C descaling:

1.Hastelloy C surface oxide and weld around the slag adhesion stronger than stainless steel, is recommended to use fine grain belt or fine grain grinding wheel.
2. Before using HNO3 / HF mixed acid pickling to blasting or grinding the oxide film break.

 

Hastelloy C Machining:

Because of the hardening sensitive, so should adopt a low cutting speed and heavy feed for processing, in order to drive into the already cold below the surface hardening.

 

Hastelloy C weld treatment :

pickling and brushing oxide

 

 