| Place of Origin: | China |
|---|---|
| Brand Name: | TORICH |
| Certification: | ISO 9001 ISO14001 TS 16949 DNV CCS |
| Model Number: | JIS G3460 |
| Minimum Order Quantity: | 5 tons |
| Price: | negotiable |
| Packaging Details: | Packed in wooden box or upon request |
| Delivery Time: | 4-8 weeks after received your payment |
| Supply Ability: | 5,000tons per year |
| Product Name: | JIS G 3460 Carbon And Nickel Steel Pipe For Low Temperature Service | Material: | Carbon And Nickel Steel |
|---|---|---|---|
| Grade: | STPL 380 STPL 450 STPL 690 | Diameter: | 5-420mm |
| Application: | For Low Temperature Service | Standard: | JIS G3460 |
| Shape: | Round | Relevant Standard: | KS D 3569 ASTM A 333 DIN 17173 DIN17174 BS3603 |
| High Light: | nickel alloy pipe,heat exchanger tubes |
||
Torich International Co.,Ltd is specialized in manufacturing and suppying JIS G 3460 Carbon and Nickel Steel Pipe for low temperature service
JIS G 3460 Steel Tube Size range:
OD: 5-420mm
WT: 0.5-50mm
Length: Upon request
JIS G 3460 Nickel Steel Pipe Application: for low temperature service
JIS G 3460 Nickel Steel Tube Shipment:
FCL, LCL workable. Bulk Vessel workable By Air, By Sea, by Courier
|
CHEMICAL COMPOSITION % max |
||||||
|
Steel grade |
C |
Si |
Mn |
P |
S |
Ni |
|
STPL 380 |
0.25 |
0.35 |
1.35 |
0.035 |
0.035 |
|
|
STPL 450 |
0.18 |
0.10-0.35 |
0.30-0.60 |
0.030 |
0.030 |
3.20-3.80 |
|
STPL 690 |
0.13 |
0.10-0.35 |
0.9 |
0.030 |
0.030 |
8.50-9.50 |
Remarks:
When it is practically difficult to apply the test due to the dimension of a pipe,STPL 380 shall , by way of compensation,contain 0.01% or more of acid soluble aluminum, or alternative,0.015% or more of total aluminum.
|
MECHANICAL PROPERTIES min |
|||
|
Steel grade |
Tensile strength Mpa |
Yeild point or proof stress Mpa |
Elongation % |
|
STPL 380 |
380 |
205 |
35 |
|
STPL 450 |
450 |
245 |
30 |
|
STPL 690 |
690 |
520 |
21 |
Remarks:
1.The value of elongation given in above table shall not be apply to the pipe whose outside diameter is under 40mm,However, the value of elongation shall be recorded.