17-4h 630 Stainless Steel Coil And Steel Bar Paint Surface
Product Details
17-4h stainless steel coil
,630 stainless steel coil
,astm paint surface ss coil
17-4PH stainless steel (630 stainless steel)
17-4PH stainless steel is a martensitic precipitation hardening stainless steel, equivalent to the Chinese brand: 0Cr17Ni4Cu4Nb. 17-4PH precipitation hardening steel with copper added. 17-4PH is used to manufacture shafts and steam turbine parts.
Chinese name 17-4PH stainless steel standard AISI, ASTM type number 17-4PH (SUS630) UNS number S17400
●17-4PH characteristics and applications:
●17-4PH chemical composition①:
| C | Mn | Si | Cr | Ni② | P | S | Cu | Niobium+tantalum Nb+Ta |
| ≤0.07 | ≤1.00 | ≤1.00 | 15.5~17.5 | 3.0~5.0 | ≤0.04 | ≤0.03 | 3.0~5.0 | 0.15~0.45 |
●17-4PH mechanical properties:
Tensile strength σb (MPa): aging at 480°C, ≥1310; aging at 550°C, ≥1060; aging at 580°C, ≥1000; aging at 620°C, ≥930
Conditional yield strength σ0.2 (MPa): aging at 480°C, ≥1180; aging at 550°C, ≥1000; aging at 580°C, ≥865; aging at 620°C, ≥725
Elongation δ5 (%): aging at 480°C, ≥10; aging at 550°C, ≥12; aging at 580°C, ≥13; aging at 620°C, ≥16
Reduction of area ψ (%): aging at 480℃, ≥40; aging at 550℃, ≥45; aging at 580℃, ≥45; aging at 620℃, ≥50
Hardness: solid solution, ≤363HB and ≤38HRC; aging at 480℃, ≥375HB and ≥40HRC; aging at 550℃, ≥331HB and ≥35HRC; aging at 580℃, ≥302HB and ≥31HRC; aging at 620℃, ≥277HB and ≥28HRC
●17-4PH heat treatment specification and metallographic structure:
Heat treatment specifications: 1) rapid cooling at 1020～1060℃; 2) aging at 480℃, after solution treatment, air cooling at 470～490℃; 3) aging at 550℃, after solution treatment, air cooling at 540～560℃; 4) Aging at 580℃, after solution treatment, air cooling at 570～590℃; 5) Aging at 620℃, after solution treatment, air cooling at 610～630℃.
Metallographic structure: The structure is characterized by precipitation hardening.
●17-4PH delivery status: generally delivered in the heat treatment state, the type of heat treatment is indicated in the contract; if it is not specified, it will be delivered in the non-heat treatment state.
Note: ①A single value is the highest value unless otherwise specified; ②When used in certain pipe making processes, the nickel content of some types of austenitic stainless steel must be slightly higher than the value shown in the table; ③ Random; ④The highest TA content is 0.10%; ⑤The highest content is 0.75%; ⑥The highest content is 0.70%
17-4PH alloy is precipitation, hardening, martensitic stainless steel.
17-4PH alloy is a precipitation, hardening, martensitic stainless steel composed of copper and niobium/columb.
This grade has high strength, hardness (up to 300°C/572°F) and corrosion resistance.
After heat treatment, the mechanical properties of the product are more perfect, and can reach a compressive strength of up to 1100-1300 mpa (160-190 ksi).
This grade cannot be used at temperatures higher than 300°C (572°F) or very low temperatures. It has good corrosion resistance to the atmosphere and diluted acids or salts. Its corrosion resistance is the same as 304 and 430.
17-4PH application field:
· Offshore platforms, helicopter decks, other platforms
· food industry
· Pulp and Paper Industry
· Aerospace (turbine blades)
· machinery parts
· Nuclear Waste Barrel
-
Auto Parts ASTM A513 Cold Rolling Welded Steel Tubes with DOM Production
Auto Parts ASTM A513 Welded Steel Tubes with DOM production ASTM A513 Electric-Resistance-Welded Carbon and Alloy Steel Mechanical Tubing Applications: for Machinery, Mechanical Engineering 1. Standard: ASTM A513 cold rolling welded precision steel tubes 2. Steel Grade: SAE1010, SAE1020, other materials upon agreement with customers. 3. Production method: Cold rolling on the weled steel tubes, to reach high accuracy on the OD and WT tolerance 4. Size range: O.D.:6-350mm W.T. -
25mm Diameter Bright Annealing Seamless Steel Tube for Hydraulic Systems
EN10305-1 E235 E355 NBK Bright Annealing Precision Steel Pipes for Hydraulic Systems EN10305-1 NBK Bright Annealed Precision steel pipes for Hydraulic system OD:4-80 (mm) WT0.5-10 (mm) Length 1000-12000mm Product name: Seamless Precision Steel Pipe Application: for hydraulic systems precision steel pipes for Hydraulic system OD (mm) WT (mm) Length (mm) 4 0.5 5800-6000 4.0 1.0 5800-6000 5.0 1.0 5800-6000 6.0 1.0 5800-6000 6.0 1.5 5800-6000 8.0 1.0 5800-6000 9.5 0.89 5800-6000 -
Precision Seamless Black Phosphating Steel Tube for Hydraulic Systems
Steel Pipes with high precision for Hydraulic Systems with Black Phosphating surface Black Phosphated Hydraulic Tubes with High Precision and tight tolerance, the tubes are produced by precision cold drawn and cold rolling, then bright annealed in a protected atmosphere, afterwards it is blackphosphated on the surface Production process: DIN series tubes, cold drawn and bright annealed precision seamless steel tube is used as the tube to be phosphated. The phosphorization is -
Precision Seamless Galvanized Steel Tubes DIN2391 EN103052 ST35.0 ST37
Precision Seamless Galvanized Steel Tubes DIN2391 EN103052 ST35.0 ST37 Production Process: Cold rolling by Cold pilger machine and Cold rolling machine,galvanized and zinc plated could be applied. Cold Rolled and Galvanized Steel Tube Production process: DIN highly accurate, cold rolled and bright seamless steel tube is used as the tube to be galvanized. The outer wall of tube is electroplated. The caps are covered at two ends of tube to prevent from the dust. Main Features: