Cold Drawn Bright Anneal 304 Stainless Steel Capillary Tubing For Medical
Contact Person : Richard SHEN
Phone Number : +86-13736164628
WhatsApp : +8613736164628
Minimum Order Quantity : | 5T | Price : | negotiable |
---|---|---|---|
Packaging Details : | packing in wooden boxes or in hexagonal bundle | Delivery Time : | 30days |
Payment Terms : | L/C, D/A, D/P, T/T, Western Union, MoneyGram | Supply Ability : | 50000T/YEAR |
Place of Origin: | China | Brand Name: | TORICH |
---|---|---|---|
Certification: | ISO9001:2008,ISO14001:2008 | Model Number: | GB/T13296 |
Detail Information |
|||
Standard: | ASTM, AISI, DIN, EN, GB, JIS, GB/T13296 | Model Number: | GB/T13296 |
---|---|---|---|
Application: | Boiler And Heat Exchanger | Thickness: | 1-14mm |
Outer Diameter: | 6-159mm | Length: | 3-12m |
High Light: | stainless tube steel,large diameter stainless steel tube |
Product Description
Product Name:TORICH GB/T13296 304/316 Seamless Stainless Steel Tubes for Boiler and Heat Exchanger
Standard:GB/T13296
Size Range: OD: 6-159mm WT: 1-14mm Length: 3-12mm or according to customers' actual application and production.
Application:for Boiler and Heat Exchanger
Steel Grade:Tp304/316/317/321/347/904/32750/32760
Technology:Hot rolled,cold drawn,cold rolled
Characteristic:
Good concentricity
Good surface quality
Good OD and ID tolerance
High Precision
Stable quality
Smooth Roughness
1 Permissible deviation of outside diameter and wall thickness
Classification | Nominal size | Allowable deviation | |
W-H | OD | ≤140 | ±1.25%D |
>140 | ±1%D | ||
S | ≤3 | -40%S | |
>3~4 | -35%S | ||
>4~5 | -33%S | ||
>5 | -28%S | ||
W-C | OD | 6~30 |
+0.15 -0.20 |
>30~50 | ±0.30 | ||
>50 | ±0.75%D | ||
S | D≤38 | +20%S | |
D>38 | -22%S |
2 Steel grade and chemical composition
Number | Steel grade | Chemical Composition % | ||||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Ti | ||
1 | 0Cr18Ni9 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
8.00~ 1.00 |
17.00~ 19.00 |
— | — |
2 | 1Cr18Ni9 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
8.00~ 10.50 |
17.00~ 19.00 |
— | — |
3 | 1Cr19Ni9 | 0.04~0.10 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
8.00~ 12.00 |
18.00~ 20.00 |
— | — |
4 | 00Cr19Ni10 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
8.00~ 12.00 |
18.00~ 20.00 |
— | — |
5 | 0Cr18Ni10Ti | ≤0.08 | ≤1.00 | ≤3.00 | ≤0.035 | ≤0.030 |
9.00~ 12.00 |
17.00~ 19.00 |
— | ≥5C |
6 | 1Cr18Ni11Ti | 0.04~0.10 | ≤0.75 | ≤2.00 | ≤0.030 | ≤0.030 |
9.00~ 13.00 |
18.00~ 20.00 |
— |
4Xc~ 0.60 |
7 | 0Cr18Ni11Nb | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
9.00~ 13.00 |
17.00~ 20.00 |
— | — |
8 | 1Cr19Ni11Nb | 0.04~0.10 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
9.00~ 13.00 |
17.00~ 20.00 |
— | — |
9 | 0Cr17Ni12Mo2 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 |
11.00~ 14.00 |
18.00~ 20.00 |
2.00~ 3.00 |
— |
10 | 1Cr17Ni12Mo2 | 0.04~0.10 | ≤0.75 | ≤2.00 | ≤0.030 | ≤0.030 |
11.0~ 14.00 |
16.00~ 20.00 |
2.00~ 3.00 |
— |
3 Recommended heat-treatment system and mechanical property
Number
|
Steel Grade | Recommended heat-treatment system | Mechanical property | |||
Tensile Strength Rm MPa |
Required Tensile Strength of Plastics Rp0.2/ MPa |
Elongation A/ % |
Density ρ/(kg/cm³) |
|||
No less than | ||||||
1 | 0Cr18Ni9 | 1010℃~1150℃ | 520 | 205 | 35 | 7.93 |
2 | 1Cr18Ni9 | 1010℃~1150℃ | 520 | 205 | 35 | 7.90 |
3 | 1Cr19Ni9 | 1010℃~1150℃ | 520 | 205 | 35 | 7.93 |
4 | 00Cr19Ni10 | 1010℃~1150℃ | 480 | 175 | 35 | 7.93 |
5 | 0Cr18Ni10Ti |
920℃ ~1150℃ |
520 | 205 | 35 | 7.95 |
6 | 1Cr18Ni11Ti |
Hot rolled≥1095℃ Cold rolled≥1050℃ |
520 | 205 | 35 | 7.93 |
7 | 0Cr18Ni11Nb |
980℃ ~1150℃ |
520 | 205 | 35 | 7.98 |
8 | 1Cr19Ni11Nb |
Hot rolled≥1095℃ Cold rolled≥1050℃ |
520 | 205 | 35 | 8.00 |
9 | 0Cr17Ni12Mo2 | 1010℃~1150℃ | 520 | 205 | 35 | 7.98 |
10 | 1Cr17Ni12Mo2 | ≥1040℃ | 520 | 205 | 35 | 7.89 |
Table 4 Hardness
Organization type | Steel grade | Hardness | ||
HBW | HRB | HV | ||
Austenitic | 00Cr18Ni10,0Cr19Ni9N,00Cr17Ni13Mo2,0Cr17Ni12Mo2N | ≤217 | ≤95 | ≤220 |
0Cr18Ni13Si4 | ≤207 | ≤95 | ≤218 | |
Others | ≤187 | 90 | 200 | |
Ferrite | 1Cr17 | ≤183 | — | — |
00Cr27Mo | ≤219 | — | — |
A.1High temperature provides non-proportional extension strength unit MPa N/ ㎜²
Steel grade | Temperature℃ | ||||||||||
100 | 150 | 200 | 250 | 300 | 350 | 400 | 450 | 500 | 550 | 600 | |
1Cr18Ni9 | 171 | 155 | 144 | 136 | 128 | 124 | 119 | 116 | 111 | 106 | — |
1Cr19Ni11Nb | 239 | 227 | 216 | 207 | 200 | 195 | 191 | 190 | 189 | 188 | — |
B.2 100 000 h Durable intensity recommended data unit MPa N/ ㎜²
Steel grade | 100 000 h Durable intensity | ||||||||||
Test temperature/℃ | |||||||||||
600 | 610 | 620 | 630 | 640 | 650 | 660 | 670 | 680 | 690 | 700 | |
1Cr18Ni9 | 95 | 88 | 81 | 74 | 68 | 63 | 57 | 52 | 48 | 43 | 40 |
1Cr19Ni11Nb | 132 | 121 | 110 | 100 | 91 | 82 | 74 | 66 | 60 | 54 | 48 |